Simulasi Analisis Kekuatan Struktur Komposit Honeycomb Sandwich Berpenguat Jenis Serat Batang Pisang dan Serat Kaca
In this study, the sandwich structure is known as a core attached to two rigid and strong shells; The core distributes the load from one shell to another. While the skin contributes to bending and turgidity, adhesives that carry shear and axial loads to the core material are used as bonding agents. As a binder in this composite used polyester resin. The honeycomb sandwich panels made are 50mm high and 50mm wide, while the panel lengths are made in three variations, namely with honeycomb lengths of 50mm, 75mm and 100mm. This honeycomb sandwich panel was tested by bending test to obtain flexural strength and stiffness values. Of the three panels that were made identically for each honeycomb core height, the highest flexural strength and stiffness figures were obtained in the panel with a honeycomb core height of 50mm, namely with a flexural strength number of 5.08kg/mm2 and a stiffness value of 12.74kg/mm.
L. Diana, A. Ghani Safitra, and M. Nabiel Ariansyah, “Analisis Kekuatan Tarik pada Material Komposit dengan Serat Penguat Polimer,” vol. 4, no.2, pp. 59–67, 2020.
M. Marsono, S. F. Hanifa, and F. Akbar, “Pembuatan dan Pengujian Panel Honeycomb Sandwich dengan Inti Berbentuk Gelombang Berbahan Komposit Serat Bambu,” J. Rekayasa Hijau, vol. 5, no. 2, pp. 165–177, 2021, doi: 10.26760/jrh.v5i2.165-177.
E. Widiyono, M. Y. Mahdum, H. Rahman, and D. Z. Noor, “Komposit Carbon Fiber Sandwich Sebagai Bahan Alternatif Pengganti Alumunium Alloy 6063 Pada Knuckle Plate Mobil Nogogeni 5 Evo,” vol. 2, 2021.
F. L. Matthews, “Composite Material Engineering And Science,” 1993.
Astroni and S. D. Handono, “Kaji Eksperimen Variasi Jenis Serat Batang Pisang Untuk Bahan Komposit Terhadap Kekuatan Mekanik.” Vol. 7 no. 2 2018.
Hexel Corporation, 2014. HexWeb Honeycomb Sandwich Design and Technology.
Takagi. 2017. “Compression Characteristics of Honeycomb Sandwich Panels to Improve Thei Impact Resistances”. Materials Science and Engineering. 1- 24-2.
Belouettar, S., Abbadi, A., Azari, Z., 2008. Experimental investigation of static and fatigue behavior of composites honeycomb materials using four point bending test. Composite Structures. Vol. 87.
American Society for Testing and Materials, 2008. Annual Book of ASTM Standards 2008 – Section 4 Volume 04.10 Wood D143. American Society for testing and materials.
Burlayenko, V.N., dan Sadowski, T., 2009, Analysis of Structural Performance of Sandwich Plates With Foam-Filled Alumunium Hexagonal Honeycomb Core, Computational Material Science, Vol.45, hal. 658-662.
Smallman, R. E. dan Bishop, R. J., 2000. “Metalurgi Fisik Modern dan Rekayasa Material”. Edisi keenam, Erlangga, Jakarta.