Analisis Kekuatan Struktur Komposit Honeycomb Sandwich Berpenguat Jenis serat Kaca dan Serat Ijuk

  • Yoggie Pratama Universitas Singaperbangsa Karawang
  • Kardiman Kardiman Universitas Singaperbangsa Karawang
  • Iman Dirja Universitas Singaperbangsa Karawang

Abstract

In this study, glass fiber and palm fiber reinforced composite materials were used with a honeycomb structure, especially a sandwich. The use of this composite material was chosen because it is environmentally friendly and can also be recycled. The use of glass fiber and fiber fiber reinforced composite materials was chosen because it is a lightweight material and also palm fiber is an abundant material and has not been utilized optimally, strong and also cheap. Material testing is done without knowing the compressive strength of the composite material itself. From the test data obtained, it shows the ability to build a honeycomb construction with the average load results being 16,979 N, 11,148 N, 10,948 N. Solidworks is a simulation software used in this study to be used to compare the maximum capacity of stress, strain and displacement results. material testing with simulation results obtained shows that the critical area for stress in each specimen is 25.92 MPa,

17.01 MPa and 16.71 Mpa

References

Diana, L., Safitra, A. G., & Ariansyah,

M. N. (2020). Analisis Kekuatan Tarik pada Material Komposit dengan Serat Penguat Polimer. Jurnal Engine: Energi, Manufaktur, dan Material, 4(2), 59-67.

Marsono, M., Hanifa, S. F., & Akbar, F. (2021). Pembuatan dan Pengujian Panel Honeycomb Sandwich dengan Inti Berbentuk Gelombang Berbahan Komposit Serat Bambu. Rekayasa Hijau: Jurnal Teknologi Ramah Lingkungan, 5(2), 165- 177.

Widiyono, E., Mahdum, M. Y., Rahman, H., & Noor, D. Z. (2021). KOMPOSIT CARBON FIBER SANDWICH SEBAGAI BAHAN ALTERNATIF PENGGANTI ALUMUNIUM ALLOY 6063 PADA KNUCKLE PLATE MOBIL NOGOGENI 5 EVO. Jurnal Nasional Aplikasi Mekatronika, Otomasi dan Robot Industri (AMORI), 2(1).

Asroni, A., & Handono, S. D. (2018). Kaji Eksperimen Variasi Jenis Serat Batang Pisang Untuk Bahan Komposit Terhadap Kekuatan Mekanik. J Teknik Mesin Univ. Muhammaddiyah Metro, 7(2), 214-21.

Prayoga, D. A., & Drastiawati, N. S. (2021). PENGARUH JUMLAH LAMINASI CORE KOMPOSIT SANDWICH SERAT KENAF DENGAN CORE KAYU SENGON TERHADAP KEKUATAN BENDING. Jurnal Teknik Mesin, 9(01), 1-10.

Muhajir, M., Mizar, M. A., & Sudjimat,

D. A. (2017). Analisis kekuatan tarik bahan komposit matriks resin berpenguat serat alam dengan berbagai varian tata letak. Jurnal Teknik Mesin, 24(2).

Prayoga, A., Eryawanto, B., & Hadi, Q. (2018). PENGARUH KETEBALAN SKIN TERHADAP KEKUATAN BENDING DAN TARIK KOMPOSIT SANDWICH DENGAN hONEYCOMB POLYPROPYLENE SEBAGAI CORE. J. Tek. Mesin, 18(1), 23-28.

Marsono, M., Ali, A., & Luwis, N. (2019). Karakteristik Mekanik Panel Honeycomb Sandwich Berbahan Komposit Fibreglass dengan Dimensi Cell-Pitch 40mm dan Cell-Height 30mm. Rekayasa Hijau: Jurnal Teknologi Ramah Lingkungan, 3(2).

Suprayogi, F., Naubnome, V., & Suci,

F. C. (2021). Pengaruh Dimensi Volume Bentuk Core Terhadap Sifat Mekanik

Published
2022-11-15
How to Cite
Pratama, Y., Kardiman, K., & Dirja, I. (2022). Analisis Kekuatan Struktur Komposit Honeycomb Sandwich Berpenguat Jenis serat Kaca dan Serat Ijuk. Jurnal Ilmiah Wahana Pendidikan, 8(22), 17-23. https://doi.org/10.5281/zenodo.7321177

Most read articles by the same author(s)

1 2 3 > >>